with a wide range of decors and colors,it' is suitable for residential and commercial buildings.
LVT FLOOR -DRY BACK STRUCTURE
|
|
LVT FLOOR -VINYL CLICK STRUCTURE
|
LVT FLOOR -LOOSE LAY STRUCTURE
|
Density | 1.8-2.02g/cm³ |
Finish Surface | EIR / Embossed / Deep crystal / Sawmill / Large crystal |
MOQ | 1 x 20'ft including 4 colors |
Dry Back | 14 pcs / bex, 65 bex / drag, 20 paquets / 20' Fcl |
Vinyl Click | 10 pcs / bex, 60 bex / drag, 20 paquets / 20' Fcl |
Loose Lay | 10 pcs / bex, 65 bex / drag, 20 paquets / 20' Fcl |
Density | 1.8-2.02g/cm³ | |
Dimensional stability | ISO23999.2008 | X Direction: 0.12% |
Curling | ISO23999.2008 | ≤0.2mm |
Residual indentation | ISO 24343-1:2007 | -0.04mm |
Light stability | IS0105-B02:Method 3 | ≥6 |
Castor chair | ISO4918 | After 25000 cycles,test specimens no visible damage |
Classification | EN ISO 10S82 | 23,31/33,42/34,43 |
Reaction to fire | EN 13501-1 | Bfl-S1 |
Slip resistance | DIN 51130:2010 EN 13893 | R10 DS |
Wear resistance | EN 660-2 | 500 grams of pressure The amount of wear ≦0.015g |
Thermal resistance | EN 12667:2001 | 0.074m²K/W |
Determination of resistanceto stains chemical resistance | ISO26987:2008 | Resistant |
Squareness | ISO24342:2007 | Deviation range: X Direction: 0.00mm~+0.05mm |
Straightness | ISO24342:2007 | Deviation range: X Direction: 0.00mm~+0.03mm |
Peel resistance | ISO 24345:2006 | X Direction: 6SN/50mm |
Determination of resistance to stubbed and burning cigarettes | EN1399:1997 Method 8 | Rating 3: Moderate change of gloss and moderate brown stain |
Utilization | Recyclable |
with a wide range of decors and colors,it' is suitable for residential and commercial buildings.
LVT FLOOR -DRY BACK STRUCTURE
|
|
LVT FLOOR -VINYL CLICK STRUCTURE
|
LVT FLOOR -LOOSE LAY STRUCTURE
|
Density | 1.8-2.02g/cm³ |
Finish Surface | EIR / Embossed / Deep crystal / Sawmill / Large crystal |
MOQ | 1 x 20'ft including 4 colors |
Dry Back | 14 pcs / bex, 65 bex / drag, 20 paquets / 20' Fcl |
Vinyl Click | 10 pcs / bex, 60 bex / drag, 20 paquets / 20' Fcl |
Loose Lay | 10 pcs / bex, 65 bex / drag, 20 paquets / 20' Fcl |
Density | 1.8-2.02g/cm³ | |
Dimensional stability | ISO23999.2008 | X Direction: 0.12% |
Curling | ISO23999.2008 | ≤0.2mm |
Residual indentation | ISO 24343-1:2007 | -0.04mm |
Light stability | IS0105-B02:Method 3 | ≥6 |
Castor chair | ISO4918 | After 25000 cycles,test specimens no visible damage |
Classification | EN ISO 10S82 | 23,31/33,42/34,43 |
Reaction to fire | EN 13501-1 | Bfl-S1 |
Slip resistance | DIN 51130:2010 EN 13893 | R10 DS |
Wear resistance | EN 660-2 | 500 grams of pressure The amount of wear ≦0.015g |
Thermal resistance | EN 12667:2001 | 0.074m²K/W |
Determination of resistanceto stains chemical resistance | ISO26987:2008 | Resistant |
Squareness | ISO24342:2007 | Deviation range: X Direction: 0.00mm~+0.05mm |
Straightness | ISO24342:2007 | Deviation range: X Direction: 0.00mm~+0.03mm |
Peel resistance | ISO 24345:2006 | X Direction: 6SN/50mm |
Determination of resistance to stubbed and burning cigarettes | EN1399:1997 Method 8 | Rating 3: Moderate change of gloss and moderate brown stain |
Utilization | Recyclable |